The corrosion characterization of a ferritic stainless steel with Mo addition in H2SO4 and HCI acid solutions

Basit Öğe Kaydı
dc.contributor.authorDemiroren, H.
dc.contributor.authorAksoy, M.
dc.contributor.authorYildiz, T.
dc.contributor.authorBuytoz, S.
dc.date.accessioned2026-08-12T17:03:27Z
dc.date.issued2009
dc.departmentFırat Üniversitesi
dc.description.abstractThe corrosion behavior of ferritic stainless steel containing 1 wt, % Mo was investigated using an AC impedance technique and the mass loss method. The alloys were produced by casting and forging. They were classified into three groups: unhomogenized, homogenized for 30 minutes and homogenized for 180 minutes. Mass loss tests were carried out on samples homogenized for 180 minutes. The corrosion tests were performed in 0.1 M H2SO4 and 0.3 M HCl acid solutions. SEM investigations were performed on the surface of samples exposed to corrosion for 30 and 360 minutes. The results were compared with results obtained from experiments performed on unalloyed ferritic stainless steel. Molybdenum (Mo) and homogenization heat treatment were found to have a beneficial effect on corrosion behavior of ferritic stainless steel in these solutions.
dc.description.sponsorshipFirat University Scientific Searches and Projects Department (FUBAP) [741]
dc.description.sponsorshipThis study was supported by project number 741 of the Firat University Scientific Searches and Projects Department (FUBAP). The authors also would like to thank Professor Mehmet Erbil of Cukurova University for his helps.
dc.identifier.doi10.1134/S2070205109050232
dc.identifier.endpage634
dc.identifier.issn2070-2051
dc.identifier.issn2070-206X
dc.identifier.issue5
dc.identifier.scopus2-s2.0-76749150557
dc.identifier.scopusqualityQ3
dc.identifier.startpage628
dc.identifier.urihttps://doi.org/10.1134/S2070205109050232
dc.identifier.urihttps://hdl.handle.net/11508/48321
dc.identifier.volume45
dc.identifier.wosWOS:000270188100023
dc.identifier.wosqualityQ4
dc.indekslendigikaynakWeb of Science
dc.indekslendigikaynakScopus
dc.language.isoen
dc.publisherMaik Nauka/Interperiodica/Springer
dc.relation.ispartofProtection of Metals and Physical Chemistry of Surfaces
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/closedAccess
dc.snmzKA_WoS_20260511
dc.subjectAlloyed Molybdenum
dc.subjectDissolution
dc.subjectPassivation
dc.subjectResistance
dc.subjectImpedance
dc.subjectBehavior
dc.subjectNickel
dc.subjectFilms
dc.titleThe corrosion characterization of a ferritic stainless steel with Mo addition in H2SO4 and HCI acid solutions
dc.typeArticle

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu